P-659

P-660

P-663

P-664

P-666

P-667

P-668

P-669

P-672

P-673

P-676

P-678

P-679

P-690

Piezoelectric coupling coefficien

k_p

0.58

0.70

0.67

0.67

0.78

0.10

0.68

0.62

0.70

0.68

0.7

0.72

0.65

0.74

k₃₁

0.32

0.39

0.38 

0.37

0.42

0.39

0.35

0.41

0.39

0.45

0.42

0.38

0.40

k₃₃

0.60

0.73

0.70 

0.70

0.78

0.70

0.68

0.72

0.70

0.80

0.72

0.70

0.75

k_t

0.42

0.46

0.45

0.45

0.50

0.45

0.46

0.44

0.46

0.46

0.50

0.47

0.46

0.48

Relative dielectric constant

ε^T₃₃ / ε₀

1100

3200

2200

2800

4500

180

2300

1400

3400

2200

6000

2750

1600

3800

Piezoelectric charge constant

d₃₃×10^-12C/N

280

700

400

480

780

70

430

250

600

430

850

540

320

710

d₃₁×10^-12C/N

-120

-350

-200

-350

-230

-130

-280

-230

-420

-260

-150

-360

Mechanical quality factor

Q_m

100

60

80

500

60

2500

90

1000

80

90

60

80

1000

70

Frequency constant

f_r·d     kH_z·cm

230

190

 200

220

180

200

230

190

200

180

190

230

190

f_r·t     kH_z·cm

210

200

200

225

200

225

200

200

Temperature characteristics

| TKf_r | (-20℃~80℃)
×10^-6 / ℃

100

260

300

120 

400 

30 

150

100

300

100

400

200

100

260

| TKC^T | (-20℃~80℃)
×10^-6 / ℃

1500

4500

5000 

2500 

6000

1800

1500

4000

2000

6000

3000

1500

4000

Curie temperature

T_c

320

220

220

230

180

450

355

340

230

325

140

280

330

210

Dielectric loss

tgδ（%）

1.20

1.80

2.00

0.50

2.60

0.70

2.00

0.30

2.30

2.00

2.60

1.50

0.40

1.80

Dielectric loss

tgδ（400V/mm，%）

1.00

1.00